Electrode Paste Self Baking Electrode for Ferrosilicon Furnace

• Feature: Long Time Materials
• Shape: Block
• Product Name: Electrode Paste
• Other Name: Carbon Electrode Paste
• Color: Black
• Size: Customized Size
• Application: Metallurgy
• Origin: China
• HS Code: 3801300000

Product Description

Product Description

Electrode paste is a conductive material for electric furnace equipment such as iron alloy furnace and calcium carbide furnace. Electrode paste is also called self-baking electrode. It relies on the heat in the ore furnace to complete the roasting. Therefore, matching the consumption rate of the electrode with the roasting speed is the key to the use of electrode paste. Due to the development of the ore furnace technology, the The development of large-scale and closed-type, the more conduction heat and radiant heat reduction obtained by the open furnace type during the baking process of the electrode is only one of conduction heat, so the heat obtained by the electrode from the furnace is greatly reduced, which It is required to improve the sintering performance of the electrode paste to make up for this deficiency.

 

Specification

Item	Electrode Paste
Si	<0.28%	Fe	<0.25%
P	<0.004%
Ash Content	2-10%	Resistivity	55-90 uΩm
V.M	10.0-15.0%	Density	>1.46g/cm3
Compression Strength	>18Mpa	Extensibility	6-20
Apparent Density	>1.42g/cm3	Rupture Strength	>4.0
Real Density	>1.98g/cm3	Fluidity Coefficient	1.10-2.10

 

Item	Specification
Ash	4.0%max	5.0%max	6.0%max	7.0% Max	9.0% Max	11.0% Max
VM	12.0%-15.5%	12.0%-15.5%	12.0%-15.5%	9.5.0%-13.5%	11.5%-15.5%	11.5%-15.5%
Compress Strength	18.0Mpa Min	17.0Mpa Min	15.7Mpa Min	19.6Mpa Min	19.6Mpa Min	19.6Mpa Min
Specific Resistance	65μΩm Max	68μΩm Max	75μΩm Max	80μΩm Max	90μΩm Max	90μΩm Max
Bulk Density	1.38G/CM3 Min	1.38G/CM3 Min	1.38G/CM3 Min	1.38G/CM3 Min	1.38G/CM3 Min	1.38G/CM3 Min

Application

1.Submerged arc furnace.
2.Ferro silicon alloy smelting.
3.Silicon manganese alloy smelting.
4.Yellow phosphorus smelting.
5.Si-Ca-Ba alloy smelting.